Plastic molding and method and apparatus for producing the same by injection molding

ABSTRACT

A plastic molding for use in an optical device, a method of producing the molding by injection molding, and an apparatus for practicing the method are disclosed. Only a part of a molding expected to sink is surely caused to sink while, e.g., a mirror surface is surely transferred to a desired part of the molding.

BACKGROUND OF THE INVENTION

[0001] The present invention relates to a lens, mirror, prism or similar plastic molding produced by injection molding and included in an optical device, e.g., a copier, laser printer, facsimile apparatus or similar image forming apparatus, and a method and an apparatus for producing the same. More particularly, the present invention is concerned with a plastic molding having, e.g., mirror surfaces and a fine undulation pattern transferred thereto with high accuracy by injection molding, and a method and apparatus for producing the same.

[0002] For injection molding, it is a common practice to use a mold assembly including a mold surface forming a cavity having a preselected volume, a transfer surface formed on the mold surface for transferring a mirror surface to a molding, and a gate open at the mold surface and having a preselected opening area. Molten resin is injected into the cavity via the gate and then cooled. The resulting molding is taken out by opening the mold assembly. While such a molding, particularly a mirror, lens, prism or similar optical element, is required to have an accurate mirror surface and a uniform refractive index, the mirror surface needing a high surface accuracy is caused to sink because the molten resin contracts at the time of solidification.

[0003] Injection molding methods for solving the above problem are taught in, e.g., Japanese Patent Laid-Open Publication Nos. 3-128218, 8-234005, 3-151218, and 3-281213 (Prior Art 1 hereinafter). In prior Art 1, a non-transfer surface or mold surface facing a transfer surface formed with, e.g., a mirror surface is roughened, or surface treatment for lowering wettability is effected, or use is made of a porous material. Injection is stopped just before a cavity is filled up with molten resin. Then, the molten metal is solidified by cooling without any dwelling. As a result the roughened surface is caused to sink due to a difference in adhering force between the molten resin, the transfer surface, and the roughened surface. This prevents the mirror from sinking. Alternatively, an overflow portion for receiving excess molten resin is located outside of the cavity. When the overflow portion begins to be filled, injection is stopped. Then, the molten resin is solidified by cooling without any dwelling. This also allows the roughened surface to sink due to a difference in adhering force between the resin, the transfer surface, and the roughened surface.

[0004] An injection molding method disclosed in Japanese Patent Laid-Open Publication No. 2-175115 (Prior Art 2 hereinafter) injects molten metal into a cavity in which a porous member communicated to a compressed gas is provided on a mold surface contacting the non-transfer surface of a molding. While dwelling and cooling are under way after the injection of the molten resin, air is fed to the non-transfer surface of the molding via the porous member. With this method, it is possible to cause a side of a cylindrical thin lens to sink.

[0005] Japanese Patent Laid-Open Publication No. 6-304973 (Prior Art 3 hereinafter) proposes an injection molding method in which a non-transfer surface is communicated to the outside air via a vent hole. During an interval between the beginning and the end of injection of molten resin into a cavity, a pressure difference is generated between the transfer surface and the non-transfer surface of the resin. As a result, the non-transfer surface of the resin is caused to sink. Specifically, air is brought into contact with the molten resin other than the mirror transferred from the transfer surface via the vent hole and a bore communicated thereto, so that the cooling speed of the resin is lowered. At the same time, a preselected air pressure is fed to the vent hole in order to generate a preselected pressure difference between the mirror portion of the resin and the vent hole. This allows only the portion of the resin facing the vent hole to sink, i.e., prevents the mirror portion from sinking. In addition, because only the vent hole portion of the resin sinks, a molding can be produced by simple control over the amount of the resin to be injected into the cavity and without any strain being generated in the resin. The resulting molding is therefore free from an internal strain and provided with an accurate mirror surface.

[0006] Prior Art 3 further teaches that the vent hole may be communicated to a compressor so as to apply a preselected air pressure to the vent hole portion of the resin. With this configuration, it is possible to generate any desired pressure difference between the mirror surface portion and the vent hole portion of the resin, thereby causing the vent hole portion to sink. In addition, the pressure difference is readily adjustable in order to further enhance the accuracy of the mirror surface without any internal strain.

[0007] Japanese Patent Laid-Open Publication No. 6-31596 (Prior Art 4 hereinafter) teaches an injection molding method causing the non-transfer surface of resin to sink. In accordance with this method, the transfer surface of a mold heated to and held at a high temperature. The transfer surface side of the resin is heated to a high temperature until the injection of molten resin into a cavity ends.

[0008] However, Prior Art 1 relying on the roughened surface, surface treatment or porous material results in an expensive mold assembly. Moreover, stopping the injection just before the cavity is filled up with the molten metal is extremely difficult. Should the timing for stopping the injection be deviated, the relation in adhering force between the transfer surface and the roughened surface would be inverted and would thereby cause the mirror surface to sink or result in short resin. In addition, because sinking cannot be provided with directionality and because setting the molding conditions is difficult, the configuration of the molding is critically limited. The filling of the molten resin may be stopped at any time lying in a broader range. However, the overflow portion formed integrally with the molding must be removed by an extra step. Moreover, should the opening area of the gate for feeding the molten resin to the overflow portion be excessively small, the relation in adhering force between the transfer surface and the roughened surface would also be inverted and would thereby cause the mirror surface to sink. Should the opening area be excessively small, the molten resin would become short.

[0009] Prior art 1 can implement a mirror or similar optical element needing a single mirror surface because it roughens the mold surface facing the transfer surface. However, Prior Art 1 cannot produce a lens, prism or similar optical element because the number and positions of mirror surfaces are limited. In addition, the relation in adhering force is inverted and causes the mirror surface to sink, depending on the material constituting the transfer surface and roughened surface and the kind of the resin.

[0010] Prior Art 2 increases the cost of the mold assembly due to the porous member and sophisticates control over the configuration of the porous member. Specifically, if the effect of the porous member is excessive, it not only admits the molten metal thereinto, but also obstructs the parting of the molding. This is particularly true when the porous portion of the porous member extends inward over the wall of the mold. Further, because the compressed gas is fed to the non-transfer surface of the molding via the porous member during the previously stated interval, a pressure difference is maintained between the non-transfer surface and the transfer surface of the resin during cooling. As a result, the internal strain remains in the resulting molding after the opening of the mold. The residual pressure not only lowers the accuracy of the transfer surface, but also causes the entire molding to deform.

[0011] Prior Art 3 generates a pressure difference between the transfer surface and the non-transfer surface of the resin during the interval mentioned earlier. This also brings about the problem stated above in relation to Prior Art 2. Prior Art 4 maintains the transfer surface of the mold at a high temperature and heats the transfer surface side of the resin to a high temperature during the previously mentioned interval. This is also undesirable in the above respect.

SUMMARY OF THE INVENTION

[0012] It is therefore an object of the present invention to provide a plastic molding capable of surely sinking only at a desired portion thereof and being surely provided with a mirror surface in another desired portion thereof, and a method and an apparatus for producing the same by injection molding.

[0013] It is another object of the present invention to provide an inexpensive and least deformable plastic molding capable of surely guiding sinking to a non-transfer surface thereof and therefore having a highly accurate transfer surface.

[0014] In accordance with the present invention, in a molding produced by an injection mold assembly having a pair of molds including a mold surface forming a cavity having a preselected volume, at least one transfer surface for transferring a mirror surface formed on the mold surface to the molding, and a gate for filling the cavity with a molten material by injection, and by injecting the molten material into the cavity via said gate and then cooling the molten material, the injection mold assembly includes at least one vent hole having a preselected opening area, and at least one bore communicated to the vent hole for applying a preselected air pressure to the molding. A step portion is formed on the mold surface between the vent hole and the transfer surface.

[0015] Also, in accordance with the present invention, in an injection molding method for producing a molding by using a mold assembly having a pair of molds including a mold surface forming a cavity having a preselected volume, at least one transfer surface for transferring a mirror surface formed the mold surfaces to the molding, and a gate for filling the cavity with a molten material by injection, and by injecting the molten material into the cavity via the gate and then cooling the molten material, the mold surface is formed with, outside of the transfer surface, at least one vent hole having a preselected opening area and at least one bore communicated to the vent hole for applying a preselected air pressure to the molding material. The air pressure is continuously generated via the vent hole even after the pressure of the molding material in the cavity has dropped to zero.

[0016] Further, in accordance with the present invention, a mold assembly has a pair of molds including a mold surface forming a cavity having a preselected volume, at least one transfer surface for transferring a mirror surface formed on the mold surface to the molding, and a gate for filling the cavity with a molten material by injection, and injects the molten material into the cavity via the gate and then cools the molten material. The mold surface is formed with, outside of the transfer surface, at least one vent hole having a preselected opening area and at least one bore communicated to the vent hole for applying a preselected air pressure to the molding material, and at least one exhaust hole located at a position adjoining the vent hole, but not facing the transfer surface.

[0017] Moreover, in accordance with the present invention, a method of producing a plastic molding begins with the step of preparing a mold assembly including at least one transfer surface and at least one none-transfer surface formed on a surface other than the transfer surface. The transfer surface and non-transfer surface forms at least one cavity. Molten resin heated to a temperature above a softening point thereof is injected into the cavity. A resin pressure is caused to act on the transfer surface to thereby cause the resin to adhere to the transfer surface, and then the resin is cooled to a temperature below the softening point. The mold assembly is opened in order to allow the resulting molding to be taken out. The temperature of at least one non-transfer surface of the resin is lowered below the temperature of the resin on the transfer surface during an interval between the beginning and the end of injection of the resin into the cavity.

BRIEF DESCRIPTION OF THE DRAWINGS

[0018] The above and other objects, features and advantages of the present invention will become more apparent from the following detailed description taken with the accompanying drawings in which:

[0019]FIG. 1 is a fragmentary view showing a conventional injection mold assembly;

[0020]FIG. 2 is a plan view showing a specific vent hole formed in the mold surface of a sink insert included in the mold assembly of FIG. 1;

[0021]FIG. 3A is a perspective view showing a specific molding produced by the mold assembly of FIG. 1;

[0022]FIG. 3B is a side elevation of the molding of FIG. 3A;

[0023]FIG. 3C is a section along line A of FIG. 3B;

[0024]FIG. 4A is a side elevation showing a specific molding produced by injection molding with an air stream flowing toward the reference surface of a cavity;

[0025]FIG. 4B is a section along line A of FIG. 4A;

[0026]FIG. 5A is a top plan view showing a specific molding produced by injection molding and caused to sink as far as its mirror surface portion;

[0027]FIG. 5B is a side elevation of the molding shown in FIG. 5 A ;

[0028]FIG. 5C is a section along line A of FIG. 5B;

[0029]FIG. 6 shows a relation between the molding produced by the mold assembly of FIG. 1 and the position of a vent hole;

[0030]FIG. 7A is a perspective view showing a molding and an injection mold assembly representative of a first embodiment of the present invention;

[0031]FIG. 7B is a fragmentary section of the mold assembly shown in FIG. 7A;

[0032]FIG. 8 is a perspective view of a molding representative of a second embodiment of the present invention;

[0033]FIG. 9A is a perspective view of a molding representative of a third embodiment of the present invention;

[0034]FIG. 9B is a section of the third embodiment in plane A1 of FIG. 9A;

[0035]FIG. 9C is a section of the third embodiment in plane A2 of FIG. 9A;

[0036]FIGS. 10A and 10B are sections each showing a particular configuration of steps included in the third embodiment in the direction of height;

[0037]FIG. 11A is a perspective view of a molding representative of a fourth embodiment of the present invention;

[0038]FIG. 11B is a section in plane A of FIG. 11A;

[0039]FIG. 12A is a perspective view of a molding representative of a fifth embodiment of the present invention;

[0040]FIG. 12B is a section in plane A of FIG. 12A;

[0041]FIG. 13A is a perspective view of a molding representative of a sixth embodiment of the present invention;

[0042]FIG. 13B is a section in plane A of FIG. 13A;

[0043]FIG. 14A is a perspective view of a molding representative of a seventh embodiment of the present invention;

[0044]FIG. 14B is a section in a plane A of FIG. 14A;

[0045]FIG. 15 is a section of a molding representative of an eighth embodiment of the present invention and including tapered steps;

[0046]FIGS. 16A and 16B are sections each showing a particular configuration of a molding representative of a ninth embodiment of the present invention;

[0047]FIG. 17 shows the variation of the internal pressure of molten resin existing in a cavity occurring from the beginning to the end of cooling of the resin, and a timing for switching an air pressure fed via a vent hole;

[0048]FIG. 18 is a section of a injection mold assembly representative of an eleventh embodiment of the present invention;

[0049]FIG. 19 is a perspective view showing a positional relation between a vent hole and an exhaust hole included in the eleventh embodiment;

[0050]FIG. 20 is a section of an injection mold assembly representative of a twelfth embodiment of the present invention;

[0051]FIG. 21 is a perspective view showing the position of an exhaust hole formed in an injection mold assembly representative of a thirteenth embodiment of the present invention;

[0052]FIG. 22 is a perspective view showing a modification of the thirteenth embodiment;

[0053]FIG. 23A is a perspective view of a plastic molding representative of a fifteenth embodiment of the present invention;

[0054]FIG. 23B is a side elevation showing a sinking region to occur in the fifteenth embodiment;

[0055]FIG. 23C is a section along line A-A of FIG. 23B;

[0056]FIG. 24A is a section showing one half of the fifteenth embodiment;

[0057]FIG. 24B is a perspective view showing cavity inserts included in the fifteenth embodiment;

[0058]FIG. 25A is a section as seen in a direction X of FIG. 24B;

[0059]FIG. 25B is a section as seen in a direction Y of FIG. 24B;

[0060]FIG. 26 is a section showing a method and an apparatus for producing a plastic molding representative of a sixteenth embodiment of the present invention;

[0061] FIGS. 27A-27D show a specific procedure available with the sixteenth embodiment;

[0062] FIGS. 28A-28D show another specific procedure available with the sixteenth embodiment;

[0063]FIG. 29 is a top plan view showing a method and an apparatus for producing a plastic molding representative of a seventeenth embodiment of the present invention;

[0064]FIGS. 30A and 30B show another specific procedure available with the seventeenth embodiment;

[0065]FIG. 31 is a top plan view showing a method and an apparatus for producing a plastic molding representative of an eighteenth embodiment of the present invention;

[0066]FIG. 32A is a perspective view showing cavity inserts included in the eighteenth embodiment;

[0067]FIG. 32B is a section as seen in a direction X of FIG. 32A;

[0068]FIG. 32C is a section as seen in a direction Y of FIG. 32A;

[0069]FIGS. 33A and 33B show another specific procedure available with the eighteenth embodiment;

[0070] FIGS. 34A-34C shows a procedure following the procedure of FIG. 32B; and

[0071]FIG. 35 shows a modification of the eighteenth embodiment.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0072] To better understand the present invention, brief reference will be made to the injection molding method taught in Prior Art 3 mentioned earlier. As shown, a mold assembly 10 is made up of a stationary mold 11 and movable mold 12, mirror pieces 13 and 14, a reference insert 15, and a sink insert 16 forming a cavity 17 having a preselected volume in cooperation. The mirror pieces 13 and 14 respectively have transfer surfaces or mold surfaces M1 and M2 for transferring mirror surfaces to a molding. The reference insert 15 has a mold surface defining the reference surface (C surface) of a molding. The sink insert 16 has a mold surface implementing a surface for causing a molding to sink (B surface). Molten resin or similar molten molding material 20 is injected into the cavity 17 via a gate, not shown. The mold surface of the sink insert 16 is formed with a vent hole 18 having a preselected opening area, and a bore 19 communicated to the vent hole 18. Air under preselected pressure is fed to the material 20 via the bore 19 and vent hole 18.

[0073]FIG. 2 shows a specific configuration of the vent hole 18 formed in the mold surface (B surface) of the sink insert 16. To feed air to the material 20, use may be made of natural draft utilizing a pressure difference between the mirror portion of the material 20 and the vent hole portion, or forced draft generating a desired pressure difference between the two portions with a compressor, not shown, communicated to the hole 18.

[0074] In the mold 10, the vent hole 18 is positioned at the side of a molding which is expected to sink. When air is fed to the cavity 17 via the bore 19 and vent hole 18, sinking successfully occurs in the expected surface of the molding. In addition, the mirror surfaces of the mirror pieces 13 and 14 are desirably transferred to the molding. The molding therefore suffers from a minimum of internal strain.

[0075] A specific molding 21 produced by the mold 10 assembly is shown in FIGS. 3A-3C. As shown, the molding is implemented as a rectangular lens having mirror surfaces (optical surfaces) 22 and 23 transferred from the mirror surfaces Ml and M2 of the mirror pieces 13 and 14, respectively. FIG. 3 shows the surface 24 of the lens 21 to be caused to sink (B surface); a sinking area is indicated by crosshatching. As shown, desired sinking is caused to occur on the B surface 24 of the lens 21. As a result, the mirror surfaces 22 and 23 are desirably transferred to the lens 21, reducing the internal strain of the lens 21.

[0076] However, the injection mold assembly 10 has the following problems left unsolved. If the various mold parts 11-16 constituting the mold 10 lack in accuracy either individually or in combination, a gap d is formed between the parts, as shown in FIG. 1. Then, air is likely to flow into the cavity 17 via the gap d and prevent the desired surface from sinking. FIGS. 4A and 4B are views similar to FIGS. 3A and 3B, showing a lens 21 molded with an air stream flowing into the reference surface side (C surface) of the cavity 17. As shown, the lens 21 fails to sink to a desired degree or practically fails to sink at its expected surface (B surface). In the worst case, a C surface 25 is caused to sink and looses surface accuracy as a reference surface.

[0077] Further, when air is introduced into the cavity 17 via the vent hole 18 by either natural draft or forced draft, it is apt to reach the mirror surfaces 22 and 23 and cause them to sink also, depending on the amount of resin filled in the cavity 17 or the amount of air. A lens or molding 21 caused to sink as far as its mirror surfaces 22 and 23 is shown in a top plan view in FIG. 5A, in a side elevation in FIG. 5B, and in a section along line A of FIG. 5B in FIG. 5C. As shown, a sunk region 27 formed in the B surface 24 extends even to the mirror surface 22 and introduces a strain in the mirror surface 22, thereby deteriorating the ability of the lens.

[0078] Preferred embodiments of the present invention will be described hereinafter. It is to be noted that reference numerals designating the structural elements of each embodiment are independent of the others, i.e., identical reference numerals do not always designate identical structural elements.

1st Embodiment

[0079]FIG. 6 shows the positional relation between the conventional molding 21 and the vent hole 18 of the mold assembly 10. The relation shown in FIG. 6 brings about the problem discussed with reference to FIGS. 5A-5C. A first embodiment of the present invention eliminates such a problem by providing a molding with steps between a vent hole and mirror surfaces.

[0080] Specifically, FIG. 7A shows a specific molding 1 representative of the first embodiment. FIG. 7B shows a part of an injection mold assembly 10 for producing the molding 1. Basically, the mold assembly 10 is similar to the conventional mold assembly 10, FIG. 1, and has its structural elements designated by the same reference numerals. The difference is that, as shown in FIG. 7B, the mold assembly 10 of the embodiment includes steps formed in a cavity 17 between a vent hole 18 and mirror surfaces and complementary in configuration to steps 6 to be formed on the molding 1.

[0081] More specifically, the molding 1 is implemented as a rectangular lens having two mirror surfaces (optical surfaces) 2 and 3 playing the role of lens surfaces. The lens 4 includes a surface 4 to be caused to sink (B surface). The steps 6 are formed on the surface 4 between the vent hole 18 and the opposite mirror surfaces 2 and 3, isolating the mirror surfaces 2 and 3 from the vent hole 18.

[0082] As shown in FIG. 7B, the mold assembly 10 includes the steps complementary in configuration to the steps 6 and formed on the mold surface between the vent hole 18 and the mirror surfaces. Just after molten resin or molding material 20 has been injected into the cavity 17, air is forced out of the cavity 17 via the vent hole 18 and a bore 19 due to the high internal pressure of the resin 20. The internal pressure of the resin 20 sequentially decreases as the resin 20 is cooled. When the pressure of the resin 20 decreases below the atmospheric pressure or below a compression pressure (when a compressor is communicated to the vent hole 18 via the bore 19), air begins to flow into the cavity 17 via the vent hole 18, causing the resin 20 to sink away from the vent hole 18. Should the steps 6 be absent on the resin 20, the resin 20 might sink as far as its mirror surfaces. In the illustrative embodiment, the steps 6 isolating the mirror surfaces 2 and 3 from the vent hole 18 tend to contract toward each other, as indicated by arrows in FIG. 7B. However, the steps of the mold assembly 10 interfere with the steps 6 and prevent them from contracting. As a result, the resin 20 and mold assembly 10 remain in close contact with each other and prevent sinking from proceeding over the steps 6, i.e., confine it to the region between the steps 6. The lens 1 is therefore caused to sink only in its expected portion and surely formed with the mirror surfaces 2 and 3 by transfer.

2nd Embodiment

[0083]FIG. 8 shows a molding 1 representative of a second embodiment of the present invention and produced by injection molding. The molding 1 is also implemented as a lens similar in configuration to the lens of FIG. 7A. As shown, a step 6 is formed on the B surface 4 of the lens 1 adjoining the vent hole, not shown, such that the step 6 surrounds the vent hole. The step 6 surrounding the vent hole prevents air from turning round and allows the sinking region to be controlled more positively than in the first embodiment.

3rd Embodiment

[0084] FIGS. 9A-9C show a molding 1 representative of a third embodiment of the present invention. The molding 1 is also implemented as a lens similar in configuration to the lens of FIG. 7A. As shown, a step 6 is formed on the side (B surface) 4 of the molding adjoining the vent hole not shown. The step 6 is substantially similar in configuration to the contour of the side 4. Specifically, when the molding 1 is a rectangular lens, the step 6 surrounds the vent hole, not shown, complementarily to the contour of the side of the lens. A sinking region can therefore be controlled in the same ratio as the sectional area of each section of the molding 1 (section A1 or A2). This successfully uniforms the internal strain and surface accuracy and thereby enhances the accuracy of the lens 1.

[0085] As shown in FIG. 10A, the steps 6 of the first to third embodiments each is implemented by projections in the direction of height. Alternatively, as shown in FIG. 10B, the steps 6 may be implemented by recesses formed in the molding 1. The recesses are also successful to control the sinking region. When the steps 6 are implemented by such recesses, the mold assembly 10 will be formed with steps in the form of projections around the vent hole 18.

4th Embodiment

[0086]FIGS. 11A and 11B show a molding 1 representative of a fourth embodiment of the present invention. As shown, steps 6 are formed on the surfaces 2 and 3 of the molding 1 which are expected to sink. This configuration also prevents air from reaching the mirror surfaces 2 and 3 via the vent hole, not shown, because the steps 6 of the molding 1 and those of the mold assembly, not shown, remain in close contact with each other.

5th Embodiment

[0087]FIGS. 12A and 12B show a molding 1 representative of a fifth embodiment of the present invention. As shown, a step 6 is formed on a part of a mirror surface 2 or 3 expected to sink. Specifically, when it is known that air will turn round to a part of the mirror surface 2 or 3 and cause it to sink beforehand, the step 6 may be formed only in such a part of the mirror surface. This configuration saves cost when a mold assembly, not shown, is formed with a step.

6th Embodiment

[0088]FIG. 13A shows a molding 1 representative of a sixth embodiment of the present invention. FIG. 13B is a section in plane A of FIG. 13A. As shown, steps 6 are formed on opposite edges of the mirror surface 2 contiguous with the B surface 4 and C surface 5, respectively. Likewise, steps 6 are formed on opposite edges of the other mirror surface 3 contiguous with the B surface 4 and C surface 5, respectively. As shown in FIG. 1, when the mold assembly 10 is not accurate, air is apt to enter the cavity 17 via an unexpected portion. As a result, as shown in FIGS. 4A and 4B specifically, air is likely to flow into the reference surface (C surface) side of the cavity 17 and turn round to the mirror surfaces 2 and 3 to cause them to sink. In the illustrative embodiment, the steps 6 formed on both longitudinal edges of the mirror surface 2 and those of the mirror surface 3 prevent air from turning round to the mirror surfaces 2 and 3 and causing them to sink.

7th Embodiment

[0089]FIG. 14A shows a molding 1 representative of a seventh embodiment of the present invention. FIG. 14B is a section in plane A of FIG. 14A. As shown, the molding 1 is identical with the molding shown in FIG. 13A except that the steps 6 facing each other on each of the mirror surfaces 2 and 3 are replaced with a single step 6 surrounding the mirror surface 2 or 3. Such steps 6 can obstruct air more positively and can therefore prevent the mirror surfaces 2 and 3 from sinking more positively.

8th Embodiment

[0090] To obstruct air tending to reach the mirror surfaces 2 and 3 of the molding 1, the steps shown in FIG. 13B or 4B suffice. FIG. 15 shows a molding configured to be easily separable from a mold. As shown, the steps 6 each is provided with a draft or draught in the direction of height h. With such steps 6, the molding can be easily separated from a mold assembly while preserving its accuracy.

9th Embodiment

[0091]FIGS. 16A and 16B each shows a particular molding representative of a ninth embodiment of the present invention. As shown, steps 6 facing each other at both edges of each mirror surface 2 or 3 are provided with a triangular cross-section (FIG. 16A) or an arcuate cross-section (FIG. 16B). This not only enhances the parting ability of the molding, but also simplifies the procedure for forming steps in, e.g., the mirror pieces 13 and 14.

[0092] In each of the eighth and ninth embodiments, the steps 6 each have a height h greater than 0.1 mm inclusive. Experiments showed that heights h greater than 0.1 mm inclusive can sufficiently obstruct air.

10th Embodiment

[0093] This embodiment relates to a method of forming a molding and will be described with reference to FIG. 7B. First, the movable mold 12 carrying the mirror piece 14 and reference insert 15 therewith is brought into contact with the stationary mold 11 loaded with the other mirror insert 13 and reference insert 15. As a result, the mold surfaces of the molds 11 and 12 form the cavity 17 having a preselected volume. A gate, not shown, is formed in a mold surface, not shown, of the mold assembly 10 in order to inject the molten resin 20 into the cavity 17. A conventional filling machine, not shown, is connected to the gate in order to fill the cavity with the molten resin 20 by injection.

[0094] Just after molten resin or molding material 20 has been injected into the cavity 17, air is forced out of the cavity 17 via the vent hole 18 and a bore 19 due to the high internal pressure of the resin 20. The internal pressure of the resin 20 sequentially decreases as the resin 20 is cooled. When the pressure of the resin 20 decreases below the atmospheric pressure or below a compression pressure (when a compressor is communicated to the vent hole 18 via the bore 19), air begins to flow into the cavity 17 via the hole 18, causing the resin 20 to sink away from the hole 18. At this instant, the steps 6 isolating the mirror surfaces 2 and 3 from the vent hole 18, as shown in, e.g., FIG. 7A, tend to contract toward each other, as indicated by arrows in FIG. 7B. However, the steps of the mold assembly 10 interfere with the steps 6 and prevent them from contracting. As a result, the resin 20 and mold 10 assembly remain in close contact with each other and prevent sinking from proceeding over the steps 6.

[0095]FIG. 17 shows how the internal pressure of the resin 20 varies from the time when the resin 20 begins to be filled in the cavity 17 to the time when it is fully cooled off. In the case where air under pressure is fed via the vent hole 18, its pressure is switched in a manner also shown in FIG. 17. As shown, in the illustrative embodiment, air is continuously fed even after the internal pressure of the resin 20 has been lowered to zero, generating air pressure in the vent hole portion. Experiments showed that the air pressure continuously generated even after the drop of the resin pressure to zero allows the sinking region to be surely controlled.

[0096] More specifically, the resin 20 remains in close contact with the mold 10 until the internal pressure of the resin 10 drops to zero, and sinking occurs thereafter. It is therefore necessary to apply the air pressured for some more period of time after the internal pressure has dropped to zero. It was found that when the molding 1 is implemented as a lens, as shown and described, the sinking region can be controlled if the air pressure is continuously applied for more than 5 seconds even after the drop of the internal pressure of the resin 20 to zero. The air pressure should preferably be higher than the atmospheric pressure (about 0.1 MPa) inclusive, but lower than 2 MPa inclusive.

[0097] The first to tenth embodiments shown and described achieve the following various unprecedented advantages.

[0098] (1) In a molding formed by an injection mold in which a pressure difference or an air pressure is generated between mirror surface portions corresponding to the mirror surfaces of a molding material and a vent hole portion corresponding to a vent hole in order to cause the material to sink, a step is formed in a cavity between the vent hole and a mirror surface portion. When the material or resin is cooled, the step prevents the resin from contracting over the step and thereby guarantees adhesion of the portions of the material other than a surface expected to sink and the mold. This prevents sinking from proceeding over the step and thereby confines it to a region delimited by the step.

[0099] (2) The step is provided on the surface of the molding facing the vent hole, so that the sinking region can be confined to such a surface.

[0100] (3) Two steps are formed in such a manner as to isolate the vent hole and the mirror surface portions, so that sinking is prevented from extending to the mirror surfaces.

[0101] (4) The step is formed to surround the vent hole in order to prevent air from turning round to the surface portions. This allows sinking to be confined to the region delimited by the step and thereby prevents sinking from extending to the mirror surfaces.

[0102] (5) When the step is similar in configuration to the contour of the side of the molding facing the vent hole, the sinking region can be controlled in the same ratio as the sectional area of the molding. This uniforms the internal strain and surface accuracy of the molding and therefore enhances the accuracy of the molding.

[0103] (6) The sinking region can be controlled both when the step or steps of the molding are implemented as projections and when they are implemented as recesses.

[0104] (7) The step or steps prevent air from reaching the mirror surface portions via the vent hole and thereby protects the mirror surface portions from sinking.

[0105] (8) The steps configured to face with each other at opposite longitudinal edges of each mirror surface obstruct air coming in through the vent hole or any other portion of the mold. This also surely protects the mirror portions from sinking.

[0106] (9) The steps each is configured to surround the associated mirror surface portion. This prevents air from reaching the mirror surfaces more positively and obviates the sinking of the mirror surface portions more positively.

[0107] (10) The steps are tapered in order to confine the sinking to the area delimited by the steps. In addition, the taper enhances the parting ability of the molding from the mold assembly.

[0108] (11) The steps are provided with a triangular or an arcuate cross-section in order to enhance the parting ability of the molding and to facilitate the formation of steps in the mold assembly.

[0109] (12) In a method of forming a molding of the kind described, an air pressure is continuously generated via the vent hole even after the internal pressure of the resin in the cavity has dropped to zero so as to control the sinking region more positively.

11th Embodiment

[0110]FIG. 18 shows an injection mold assembly representative of an eleventh embodiment of the present invention. As shown, a sink insert 5 is located at a position where sinking is expected to occur. The sink insert 5 is formed with a vent hole 7, a bore 8 communicated to the vent hole 7, and a pair of exhaust holes 20 respectively positioned above and below the vent hole 7 and bore 8. FIG. 19 shows a positional relation between the vent hole 7 and the exhaust holes 20.

[0111] In the illustrative embodiment, just after molten resin or molding material 10 has been injected into a cavity 6, it is difficult for air 9 fed under pressure via the vent hole 7 to enter the cavity 6. The internal pressure of the resin 10 sequentially decreases as the resin 10 is cooled. When the pressure of the resin 10 decreases below the pressure of the compressed air 9 delivered to the vent hole 7, the air 9 begins to flow into the cavity 6 via the vent hole 7. As a result, the portion of the resin 10 corresponding to one side 15 of a molding 11, FIG. 19, and facing the vent hole 7 begins to sink (X4) away from the inner periphery of the cavity 6. The compressed air 9 introduced into the cavity 6 hits against the resin 10 and then discharged from the cavity 6 via the exhaust holes 20. That is, the compressed air 9 is prevented from turning round to the upper surface 12 and lower surface 13 of the molding 11 which should turn out mirror surfaces. If desired, a machine for forced exhaustion may be connected to the bore 8 in order to promote more effective discharge of the compressed air 9. When the mold assembly is used to form, e.g., a lens of resin applicable to an image forming apparatus or similar optical apparatus, the exhaust holes 20 should be 0.001 mm to 0.5 mm wide (vertical dimension in FIG. 18). With such a width, the exhaust holes 20 allow a minimum of resin to enter it and thereby frees the molding 11 from burrs.

12th Embodiment

[0112]FIG. 20 shows a mold representative of a twelfth embodiment of the present invention. As shown, this embodiment is identical with the eleventh embodiment except that the exhaust holes 20 are implemented by porous members 21.

13th Embodiment

[0113]FIG. 21 shows the position of an exhaust hole formed in an injection mold assembly representative of a thirteenth embodiment of the present invention. As shown, a continuous exhaust hole 22 is formed to surround the vent hole 7. The exhaust hole 22 may also be implemented by the porous member 21 in order to simplify the configuration of the insert 5, FIG. 20.

14th Embodiment

[0114]FIG. 22 shows a fourteenth embodiment of the present invention which is a modification of the thirteenth embodiment. As shown, this embodiment is identical with the thirteenth embodiment except that an exhaust hole 23 is similar configuration to the contour of the side of the molding 11 which is expected to sink. Again, the exhaust hole 23 may be implemented by the porous member 21 in order to simplify the configuration of the insert 5, FIG. 20.

[0115] The eleventh to fourteenth embodiments shown and described have the following unprecedented advantages.

[0116] (1) At least one exhaust hole is formed in the vicinity of a vent hole used to feed air under -pressure for sinking. The exhaust hole discharges air caused sinking to occur in the vicinity of the vent hole to the outside of a mold assembly before it reaches portions expected to form mirror surfaces. Therefore, air is prevented from reaching portions other than the portion to sink, so that the shape of the mold assembly is surely transferred to the other portions of the molding.

[0117] (2) A single exhaust hole surrounds the vent hole and discharges air caused to sinking to occur smoothly to the outside of the mold assembly. This guides air only to the portion of the molding expected to sink more positively.

[0118] (3) The or each exhaust hole is implemented by a porous member. Therefore, particularly when a single exhaust hole surrounds the vent hole, the member formed with the holes is simple in structure.

[0119] (4) Air is forcibly discharged via the exhaust holes, so that air caused sinking to occur in the cavity can be discharged more smoothly.

[0120] (5) The exhaust hole has an opening width as small as 0.001 mm to 0.5 mm and prevents a molding material from entering it. This frees the resulting molding from burrs.

15th Embodiment

[0121] FIGS. 23A-23C show a plastic molding formed by a method representative of a fifteenth embodiment of the present invention. The molding may be implemented not only as a lens but also as a mirror, prism or similar optical device. As shown, a molding 1 has mirror surfaces or transfer surfaces 1 a and 1 b on its top and bottom, respectively. In addition, the molding 1 has a reference surface or non-transfer surface 1 c at one side and a sink surface or non-transfer surface 1 d at the other side. The reference surface 1 c is to be mounted to another part while the sink surface 1 d is expected to sink.

[0122] Reference will be made to FIGS. 24A, 24B, 25A and 25B for describing a molding apparatus 2 for producing the above molding 1. As shown, the molding apparatus 2 includes a stage 3 loaded with a lower mold 4. An upper mold 5 is positioned above the lower mold 4 and movable into and out of contact with the lower mold 4 by being driven by a clamping device, not shown.

[0123] A plurality of (four in the embodiment) inserts are interposed between the lower mold 4 and the upper mold 5 and constitute cavity inserts. Specifically, mirror inserts 6 and 7 facing each other are respectively formed with mirror surfaces 6 a and 7 a for forming the mirror surfaces 1 a and 1 b of the molding 1. A reference insert 8 and a sink insert 9 face each other at both sides of the mirror inserts 6 and 7 and are respectively formed with non-transfer surfaces 8 a and 9 a in order to form the reference surface 1 c and sink surface 1 d. The surfaces of the inserts 6-9 form a cavity 10. The non-transfer surfaces 8 a and 9 a each is formed with fine irregularities or undulation.

[0124] It is to be noted that FIGS. 24A and 24B show only one half of the molding apparatus 2; the other half is also provided with cavity inserts identical with the cavity inserts 6-9. A sprue, not shown, is formed in the upper mold 5 while a sprue 6 b is formed in the mirror insert 6 and communicable to the above sprue. An injection molding machine, not shown, feeds molten resin to the cavity 10 via the sprue of the upper mold 5 and sprue 6 b.

[0125] A vent hole 11 is formed in the sink insert 9. The vent hole 11 is open to the cavity 10 at one end and connected to a feed tube 12 at the other end. The feed tube 12 is interposed between the lower mold 4 and the upper mold 5 and connected to a gas feed unit 14 via a temperature control unit 13. A gas, e.g., air compressed to a preselected pressure by the gas feed unit 14 and controlled to a preselected temperature by the temperature control unit 13 is fed via the feed tube 12.

[0126] In the illustrative embodiment, molten resin heated above its softening point is injected into the cavity 10 of the mold assembly heated to a temperature lower than the softening point of the resin. Therefore, the temperature control unit 13 controls the gas to a temperature about 3° C. lower than the temperature of the mirror inserts 6 and 7 and reference insert 8. It follows that the temperature of the gas fed from the feed tube 11 to the sink surface 1 d is lower than the temperature of the mirror surfaces 1 a and 1 b and reference surface 1 c. The lower mold 4 and upper mold 5 surrounding the inserts 6-9 each is provided with a temperature control mechanism including a heater and an oil cooler, not shown. The heater and oil cooler respectively heat and cool the associated molds 4 and 5 and therefore the inserts 6-9.

[0127] In the illustrative embodiment, the temperature control unit 13 and gas feed unit 14 constitute a feeding device, and constitute gas feeding means in combination with the vent hole 11.

[0128] The operation of the above arrangement will be described hereinafter. When a lens or similar plastic optical element is produced by conventional injection molding, molding conditions allowing the entire area to be transferred (allowing the internal pressure of the molding to drop substantially to zero at the time of take-out) are set up.

[0129] However, because molten resin is sharply cooled as soon as it is introduced into a mold, the resulting temperature distribution, pressure distribution, density distribution and so forth disturb the shape of a molding. This, coupled with the internal strain (deflection) of the resin, adversely influences the optical characteristic of the molding. Although the transfer of the mold configuration, internal strain and deformation may be reduced if a molding is caused to partly sink, it is extremely difficult to specify the part of a molding to sink. This embodiment is significant in that it can specify the part of a molding to sink, as follows.

[0130] While the mold assembly is held at a temperature lower than the softening point of resin, molten resin A heated above its softening point is injected into the cavity 1 0. Then, a resin pressure is caused to act on the transfer surfaces 6 a and 7 a of the mirror inserts 6 and 7, respectively. At the same time as the injection of the resin A, a cool gas compressed to a preselected pressure by the air feed unit 14 and controlled to a preselected temperature by the temperature control unit 13 is fed to the sink surface 1 d via the vent hole 11. The feed of the gas is continued until the resin A has been fully injected into the cavity 10. At this instant, the sink surface 1 d lower in temperature than the mirror surfaces 1 a and 1 b solidifies first and increases its viscosity. This makes it difficult for the sink surface 1 d to remain in contact with the non-transfer surface 9 a of the sink insert 9 before the end of the injection of the resin A. After the injection of the resin A and the following stop of feed of the cool gas, the cavity 10 is caused to dwell at a preselected pressure and cooled. As soon as the pressure inside the cavity 10 drops substantially to zero, the upper mold 5 is opened away from the lower mold 4. Subsequently, the molding 1 is taken out of the cavity 10.

[0131] The sink surface 1 d of the molding 1 obtains a parting ability earlier than the other surfaces of the same. As a result, the sink surface 1 d begins to sink earlier than the other surfaces contacting the inserts 6-8. This successfully prevents the mirror surfaces 1 a and 1 b from sinking and thereby allows the desired mirror surfaces 1 a and 1 b to be faithfully transferred to the molding 1 in a short molding cycle.

[0132] Moreover, the sink surface 1 d is held at a temperature lower than the temperature of the resin A from the end of the resin injection to the beginning of cooling. Consequently, a temperature difference does not occur between the mirror surfaces 1 a and 1 b and the sink surface 1 d during cooling, so that an internal strain is prevented from remaining in the molding after the opening of the mold assembly. This not only prevents the accuracy of the mirror surfaces 1 a and 1 b from decreasing, but also prevents the entire molding I from deforming.

[0133] In addition, the gas feeding means can be implemented only if the vent hole 11 is formed in the sink insert 9 and connected to the temperature control unit 13 and gas feed unit 14. The mold assembly is therefore simple in construction.

16th Embodiment

[0134] Referring to FIGS. 26, 27A-27D and 28A-28D, a method and an apparatus for producing a plastic molding representative of a sixteenth embodiment of the present invention will be described. A molding to be produced by this embodiment is identical in configuration with the molding of the fifteenth embodiment and will be described with reference to FIGS. 23A-23C. Structural elements identical with the elements of the fifteenth embodiment are designated by identical reference numerals and will not be described specifically in order to avoid redundancy.

[0135] As shown in FIGS. 26 and 27A-27D, a plurality of (four in the embodiment) inserts are interposed between the lower mold 4 and the upper mold 5 and constitute cavity inserts. Specifically, mirror inserts 16 and 17 facing each other are respectively formed with mirror surfaces 16 a and 17 a for forming the mirror surfaces 1 a and 1 b of a molding. A reference insert 18 and a sink insert 19 face each other at both sides of the mirror inserts 16 and 17 and are respectively formed with non-transfer surfaces 18 a and 19 a in order to form the reference surface 1 c and sink surface 1 d of the molding. The surfaces of the inserts 16-19 form a cavity 20. The non-transfer surfaces 18 a and 19 a each is formed with fine irregularities.

[0136] A sprue, not shown, is formed in the upper mold 5 while a sprue 6 b is formed in the mirror insert 16 and communicable to the above sprue. An injection molding machine, not shown, injects molten resin into the cavity 20 via the sprue of the upper mold 5 and sprue 16 b. A vent hole 21 is formed in the sink insert 19. The vent hole 21 is open to the cavity 20 at one end and connected to a feed tube 22 at the other end. The feed tube 22 is interposed between the lower mold 4 and the upper mold 5.

[0137] The feed tube 22 is connected to a gas feed unit 23. The gas feed unit 23 feeds a gas, e.g., air compressed to a preselected pressure to between the sink surface 1 d and the transfer surface 19 a via the feed tube 22 and vent hole 21. In this embodiment, the gas feed unit 23 constitutes a feeding device and constitutes gas feeding means in combination with the vent hole 21 and feed tube 22.

[0138] The operation of the illustrative embodiment will be described with reference to FIGS. 27A-27D. As shown, while the mold assembly is held at a temperature lower than the softening point of resin, molten resin A heated above its softening point is injected into the cavity 20. Then, a resin pressure is caused to act on the transfer surfaces 16 a and 17 a of the mirror inserts 16 and 17, respectively. At the same time as the injection of the resin A, a gas compressed to a preselected pressure by the air feed unit 23 is fed to between the sink surface 1 d and the non-transfer transfer surface 19 a. The feed of the gas is continued until the resin A has been fully injected into the cavity 20 (see FIGS. 27A and 27B). At this instant, a gas layer is formed between the non-transfer surface 19 a and the sink surface 1 d, making it difficult for the sink surface 1 d to remain in contact with the non-transfer surface 19 a before the end of the injection of the resin A.

[0139] After the injection of the resin A and the following stop of feed of the gas, the cavity 20 is caused to dwell at a preselected pressure and cooled. As a result, the gas layer between the sink surface 1 d and the non-transfer surface 19 a is compressed by the internal pressure of the resin A, but remains between them (see FIG. 27C). Such residual gas expands as the internal pressure approaches zero, separating the sink surface id from the non-transfer surface 19 a. When the internal pressure reaches zero, the non-transfer surface 19 a obtains a parting ability earlier than the other surfaces. When the pressure inside the cavity 20 drops substantially to zero, the upper mold 5 is released from the lower mold 4. Subsequently, the molding 1 is taken out of the cavity 20.

[0140] In this manner, the sink surface 1 d begins to sink earlier than the other surfaces contacting the inserts 16-18. This successfully prevents the mirror surfaces 1 a and 1 b from sinking and thereby allows the desired mirror surfaces 1 a and 1 b to be faithfully transferred to the molding 1 in a short molding cycle. Moreover, the gas layer remains between the sink surface 1 d and the non-transfer surface 19 a until the cooling step begins after the injection of the molten resin, preventing the pressure difference between the mirror surfaces 1 a and 1 b and the sink surface 1 d from increasing during cooling. Consequently, the internal strain of the molding 1 is prevented from remaining after the opening of the mold assembly. This not only prevents the accuracy of the mirror surfaces 1 a and 1 b from decreasing, but also prevents the entire molding 1 from deforming.

[0141] This embodiment may be practiced with the same configuration as the fifteenth embodiment, as follows. The gas fed from the gas feed unit 23 is controlled to substantially the same temperature as the mold by the temperature control unit 31 shown in FIG. 15. In this case, as shown in FIGS. 28A-28D, while the mold assembly is held at a temperature lower than the softening point of resin, molten resin heated above its softening point is injected into the cavity 20. Then, a resin pressure is caused to act on the transfer surfaces 6 a and 7 a of the mirror inserts 6 and 7, respectively. At the same time as the injection of the resin, the gas compressed to a preselected pressure by the gas feed unit 23 is fed to between the sink surface 1 d and the non-transfer surface 9 a. The feed of the gas is continued until the resin A has been fully injected into the cavity 10 (see FIGS. 28A and 28B). At this instant, a gas layer is formed between the non-transfer surface 9 a and the sink surface 1 d, making it difficult for-the sink surface 1 d to remain in contact with the non-transfer surface 9 a before the end of the injection of the resin.

[0142] After the injection of the resin and the following stop of feed of the gas, the cavity 10 is caused to dwell at a preselected pressure and cooled. As a result, the gas layer between the sink surface 1 d and the non-transfer surface 9 a is compressed by the internal pressure of the resin, but remains between them (see FIG. 28C). The residual gas expands as the internal pressure approaches zero, separating the sink surface 1 d from the non-transfer surface 9 a. When the internal pressure reaches zero, the non-transfer surface 9 a obtains a parting ability earlier than the other surfaces (see FIG. 28D). When the pressure inside the cavity 10 drops substantially to zero, the upper mold 5 is released from the lower mold 4. Subsequently, the molding 1 is taken out of the cavity 10.

17th Embodiment

[0143] A method and an apparatus for producing a plastic molding representative of a seventeenth embodiment of the present invention will be described with reference to FIGS. 29, 30A and 30B. A molding to be produced by this embodiment is identical in configuration with the molding of the fifteenth embodiment and will be described with reference to FIGS. 23A-23C. Structural elements identical with the elements of the fifteenth embodiment will be designated by identical reference numerals and will not be described specifically in order to avoid redundancy.

[0144] As shown, a plurality of (four in the embodiment) inserts are interposed between the lower mold 4 and the upper mold 5 and constitute cavity inserts. Specifically, mirror inserts 26 and 27 facing each other are respectively formed with mirror surfaces 26 a and 27 a for forming the mirror surfaces 1 a and 1 b of a molding. A reference insert 28 and a sink insert 29 face each other at both sides of the mirror inserts 26 and 27 and are respectively formed with non-transfer surfaces 28 a and 29 a in order to form the reference surface 1 c and sink surface 1 d of the molding. The surfaces of the inserts 16-19 form a cavity 30. The non-transfer surfaces 28 a and 29 a each is formed with fine irregularities.

[0145] A sprue, not shown, is formed in the upper mold 5 while a sprue 26 b is formed in the mirror insert 26 and communicable to the above sprue. An injection molding machine, not shown, injects molten resin into the cavity 30 via the sprue of the upper mold 5 and sprue 26 b. A vent hole 31 is formed in the sink insert 29. One end of the vent hole 31 is communicated to a gas feed unit 36 via a vent hole 32 formed in the lower mold and a feed tube 34. The other end of the vent hole 31 is communicated to the outside of the mold assembly via a exhaust tube 35.

[0146] The gas feed unit 36 feeds gas, e.g., air controlled to a preselected pressure and a preselected temperature to the vent hole 31 via the feed tube 34 and vent hole 32, and then discharges it via the vent hole 33 and exhaust tube 35. The gas therefore cools the non-transfer surface 29 a of the sink insert 29.

[0147] In the illustrative embodiment, molten resin heated above its softening point is injected into the cavity 30 of the mold heated to a temperature tower than the softening point of the resin. Therefore, a temperature control unit 36 controls the temperature of the gas to a temperature about 3° C. lower than the temperature of the mirror inserts 26 and 27 and reference insert 28. It follows that the temperature of the gas fed from the vent hole 31 to the sink surface 29 is lower than the temperature of the mirror surfaces 26 a and 27 a and non-transfer surface 28 a.

[0148] In this embodiment, the gas feed unit 36, feed tube 34, vent holes 31-33 and exhaust tube 35 constitute cooling means.

[0149] In operation, before the injection of molten resin, a cool gas controlled to a preselected pressure and a preselected temperature is fed from the gas feed unit 36 to the non-transfer surface 29 a via the vent hole 31 so as to cool the non-transfer surface 29 a. Then, while the mold assembly is held at a temperature lower than the softening point of resin, molten resin A heated above its softening point is injected into the cavity 30. Subsequently, a resin pressure is caused to act on the transfer surfaces 26 a and 27 a of the mirror inserts 26 and 27, respectively. The feed of the cool gas is continued until the resin A has been fully injected into the cavity 30. At this instant, the sink surface 1 d lower in temperature than the mirror surfaces 1 a and 1 b solidifies first and increases its viscosity, making it difficult for the sink surface 1 d to remain in contact with the non-transfer surface 29 a before the end of the injection of the resin A. After the injection of the molten resin and the following stop of feed of the cool gas, the cavity 30 is caused to dwell at a preselected pressure and cooled. When the pressure inside the cavity 30 drops substantially to zero, the upper mold 5 is released from the lower mold 4. Subsequently, the molding I is taken out of the cavity 20. This embodiment achieves the same advantages as the fifteenth embodiment.

18th Embodiment

[0150] A method and an apparatus for producing a plastic molding representative of a seventeenth embodiment of the present invention will be described with reference to FIGS. 3 1, 32A-32C, 33A, 33B, 34A-34C and 35. A molding to be produced by this embodiment is identical in configuration with the molding of the fifteenth embodiment and will be described with reference to FIGS. 23A-23C. Structural elements identical with the elements of the fifteenth embodiment will be designated by identical reference numerals and will not be described specifically in order to avoid redundancy.

[0151] As shown, a plurality of (four in the embodiment) inserts are interposed between the lower mold 4 and the upper mold 5 and constitute cavity inserts. Specifically, mirror inserts 41 and 42 facing each other are respectively formed with mirror surfaces 41 a and 42 a for forming the mirror surfaces 1 a and 1 b of a molding. A reference insert 43 and a sink insert 44 face each other at both sides of the mirror inserts 41 and 42 and are respectively formed with non-transfer surfaces 43 a and 44 a in order to form the reference surface 1 c and sink surface 1 d. The surfaces of the inserts 4144 form a cavity 45. The non-transfer surfaces 44 a and 45 a each is formed with fine irregularities.

[0152] A sprue, not shown, is formed in the upper mold 5 while a sprue 41 b is formed in the mirror insert 41 and communicable to the above sprue. An injection molding machine, not shown, injects molten resin into the cavity 45 via the sprue of the upper mold 5 and sprue 41 b. A vent hole 46 is formed in the sink insert 44. The vent hole 46 is open to the cavity 45 at one end and connected to a bore 47 at the other end. The bore 47 is communicated to a flow rate control unit 50 via a vent hole 48 formed in the lower mold 4 and a feed tube 49. The flow rate control unit 50 is connected to a gas feed unit 53 via a pressure control unit 51 and a temperature control unit 52.

[0153] The gas feed unit 53 constitutes a gas source. The temperature control unit 52 controls the temperature of a gas fed from the gas feed unit 53. The pressure control unit 51 controls the pressure of the gas fed from the gas feed unit 53. Further, the flow rate control unit 50 controls the flow rate of the gas fed from the gas feed unit 53. The vent hole 47 is communicated to an exhaust valve 56 via a vent hole 54 formed in the lower mold 5 and an exhaust tube 55. The gas fed from the gas feed unit 53 to the vent hole 47 is discharged to the outside when the exhaust valve 56 is open, or introduced into the cavity 45 when the valve 56 is closed.

[0154] In this embodiment, the flow rate control unit 50, pressure control unit, temperature control unit 52 and gas feed unit 53 constitute a feeding device. The feeding device constitutes gas feeding means in combination with the vent holes 46, 47, 48 and 54, feed tube 49, and exhaust valve 56.

[0155] The operation of the illustrative embodiment will be described with reference to FIGS. 33A, 33B and 34A-34C. Briefly, this embodiment is characterized in that a step of pressing the sink surface 1 d of molten metal with the gas is combined with at least one of a step of lowering the temperature of the sink surface 1 d below the temperature of the mirror surfaces 1 a and 1 b, a step of forming a gas layer between the sink surface 1 d and the sink insert 44, and a step of lowering the temperature of the sink insert 44 facing the sink surface 1 d below the temperature of the mirror inserts 41 and 42. The following description will concentrate on the combination of all of such steps.

[0156] First, the exhaust valve 56 is opened to feed a small amount of gas to the vent hole 47 via the flow rate control unit 50, thereby cooling the sink insert 44 (see FIG. 33A). Specifically, the flow rate of the gas is so selected as to prevent the gas from entering the cavity 45; otherwise, the gas would enter the cavity 45 and cool even the mirror surfaces 41 and 42. If desired, the temperature of the gas may be controlled in order to promote the effective cooling of the sink insert 44.

[0157] After the mold assembly has been heated to a temperature lower than the softening point of resin, but before molten resin heated to a temperature above its softening point is injected into the cavity 45, the flow rate and pressure of the gas are increased by the flow rate control unit 50 and pressure control unit 51, respectively. As a result, the gas is admitted into the cavity 45. Subsequently, the molten resin begins to be injected into the cavity 45 (see FIG. 33B). The increase in the flow rate of the gas promotes the cooling of the resin while the increase in the pressure of the gas allows the gas to press the sink surface 1 d and allows a gas layer to be formed between the sink surface 1 d and the sink insert 44.

[0158] After the injection of the resin (see FIG. 34A), the exhaust valve 56 is closed while the pressure of the gas is adequately controlled by the pressure control unit 51. As a result, the cavity 45 is caused to dwell at a preselected pressure and cooled (see FIGS. 34B and 34C). When the pressure inside the cavity 45 drops substantially to zero, the upper mold 5 is released from the lower mold 4. Thereafter, the molding 1 is taken out of the cavity 45.

[0159] This embodiment achieves the same advantages as the fifteenth embodiment, and in addition achieves an advantages that the sink surface 1 d is constantly pressed and therefore easily separates from the sink insert 44. This allows the sink surface 1 d to sink more positively.

[0160]FIG. 35 shows an alternative arrangement wherein the flow control unit 50 is connected to a gas conduitwork 57 available in a factory.

[0161] Constantly pressing the sink surface 1 d, as shown and described, is not essential. Alternatively, there may be used at least one of three different methods: lowering the temperature of at least one of the non-transfer surfaces of the resin below the temperature of the transfer surfaces from the beginning to the end of the injection of the resin, forming a gas layer between at least one of the non-transfer surfaces of the resin and the mold assembly, and lowering the temperature of the mold portion facing at least one of the non-transfer surfaces of the resin below the temperature of the mold portion facing the transfer surfaces.

[0162] The fifteenth to eighteenth embodiments shown and described have the following unprecedented advantages.

[0163] (1) The non-transfer surface of a molding obtains a parting ability earlier than the other surfaces of the same. This successfully prevents the transfer surfaces of the molding from sinking and thereby allows desired mirror surfaces to be faithfully transferred to the molding in a short molding cycle.

[0164] (2) The non-transfer surface of molten resin is held at a temperature lower than the temperature of the transfer surfaces from the end of resin injection to the beginning of cooling. Consequently, a temperature difference does not occur between the transfer surfaces and the non-transfer surfaces during cooling, so that an internal strain is prevented from remaining in the molding after the opening of a mold assembly. This not only prevents the accuracy of the transfer surfaces from decreasing, but also prevents the entire molding from deforming.

[0165] (3) A gas layer is formed between the non-transfer surface of the resin and the mold assembly until the cooling step begins after the injection of the molten resin, preventing the pressure difference between the transfer surfaces and the non-transfer surface from increasing during cooling. Consequently, the internal strain of the molding is prevented from remaining after the opening of the mold assembly. This not only prevents the accuracy of the transfer surfaces from decreasing, but also prevents the entire molding from deforming.

[0166] (4) The gas layer is formed between the non-transfer surface of the resin and the mold and/or the temperature of the non-transfer surface is held lower than the temperature of the transfer surface until the cooling step begins after the injection of the molten resin, thereby preventing a difference in temperature or pressure between the transfer surface and the non-transfer surface from increasing during cooling. Consequently, the internal strain of the molding is prevented from remaining after the opening of the mold assembly. This not only prevents the accuracy of the transfer surfaces from decreasing, but also prevents the entire molding from deforming.

[0167] (5) The temperature of the non-transfer surface of the resin is lowered, the non-transfer surface is pressed, and/or the gas layer is formed between the non-transfer surface of the resin and the mold. This allows the non-transfer surface to sink with priority by use of a simple construction.

[0168] (6) Gas feeding means can be implemented only if a vent hole is formed in the mold and communicated to a feeding device. This prevents the mold configuration from being complicated.

[0169] (7) By cooling the non-transfer surface of the mold assembly with cooling means, it is possible to cool the non-transfer surface of the resin. The non-transfer surface can therefore be caused to sink by an inexpensive construction.

[0170] Various modifications will become possible for those skilled in the art after receiving the teachings of the present disclosure without departing from the scope thereof. For example, while the embodiments have concentrated on a molding in the form of a rectangular lens (having two mirror surfaces or optical surfaces), the present invention is similarly applicable to, e.g., a mirror having a single mirror surface or a prism having a plurality of mirror surfaces. 

What is claimed is:
 1. In a molding produced by an injection mold assembly having a pair of molds including a mold surface forming a cavity having a preselected volume, at least one transfer surface for transferring a mirror surface formed on said mold surface to said molding, and a gate for filling said cavity with a molten material by injection, and by injecting said molten material into said cavity via said gate and then cooling said molten material, said injection mold assembly includes at least one vent hole having a preselected opening area, and at least one bore communicated to said vent hole for applying a preselected air pressure to said molding, and a step portion formed on said mold surface between said vent hole and said transfer surface.
 2. A molding as claimed in claim 1 , wherein either a pressure difference or an air pressure is generated between said transfer surface and a vent hole portion of said molding facing said vent hole to thereby cause said vent hole portion to sink.
 3. A molding as claimed in claim 2 , wherein said step portion is formed on said mold surface where said vent hole is present.
 4. A molding as claimed in claim 3 , wherein said step portion isolates said vent hole and said transfer surface.
 5. A molding as claimed in claim 3 , wherein said step portion comprises a single step surrounding said vent hole.
 6. A molding as claimed in claim 3 , wherein said step portion comprise a single step similar in configuration to a contour of the mold surface where said vent hole is present.
 7. A molding as claimed in claim 2 , wherein said step portion isolates said vent hole and said transfer surface.
 8. A molding as claimed in claim 2 , wherein said step portion comprises a single step surrounding said vent hole.
 9. A molding as claimed in claim 2 , wherein said step portion comprise a single step similar in configuration to a contour of the mold surface where said vent hole is present.
 10. A molding as claimed in claim 2 , wherein said step portion comprises a projection.
 11. A molding as claimed in claim 2 , wherein said step portion comprises a recess.
 12. A molding as claimed in claim 2 , wherein said step portion is provided on said transfer surface.
 13. A molding as claimed in claim 12 , wherein said step portion comprises a pair of steps so configured as to sandwich a longitudinal surface of said transfer surface.
 14. A molding as claimed in claim 12 , wherein said step portion comprises a single step so configured as to surround said transfer surface.
 15. A molding as claimed in claim 2 , wherein said step portion comprises a pair of steps so configured as to sandwich a longitudinal surface of said transfer surface.
 16. A molding as claimed in claim. 2, wherein said step portion comprises a single step so configured as to surround said transfer surface.
 17. A molding as claimed in claim 2 , wherein said step portion is tapered in a cross section.
 18. A molding as claimed in claim 2 , wherein said step portion is triangular in a cross-section.
 19. A molding as claimed in claim 2 , wherein said step portion is arcuate in cross section.
 20. A molding as claimed in claim 2 , wherein said step portion has a height greater than 0.1 mm inclusive.
 21. In an injection molding method for producing a molding by using a mold assembly having a pair of molds including a mold surface forming a cavity having a preselected volume, at least one transfer surface for transferring a mirror surface formed said mold surfaces to said molding, and a gate for filling said cavity with a molten material by injection, and by injecting said molten material into said cavity via said gate and then cooling said molten material, said mold surface is formed with, outside of said transfer surface, at least one vent hole having a preselected opening area and at least one bore communicated to said vent hole for applying a preselected air pressure to said molding material, and the air pressure is continuously generated via said vent hole even after a pressure of said molding material in said cavity has dropped to zero.
 22. A method as claimed in claim 21 , wherein either a pressure difference or an air pressure is generated between said transfer surface and a vent hole portion of said molding facing said vent hole.
 23. A method as claimed in claim 22 , wherein the air pressure is higher than an atmospheric pressure (about 0.1 MPa) inclusive, but lower than 2 MPa inclusive.
 24. A mold assembly having a pair of molds including a mold surface forming a cavity having a preselected volume, at least one transfer surface for transferring a mirror surface formed on said mold surface to said molding, and a gate for filling said cavity with a molten material by injection, and injecting said molten material into said cavity via said gate and then cooling said molten material, said mold surface is formed with, outside of said transfer surface, at least one vent hole having a preselected opening area and at least one bore communicated to said vent hole for applying a preselected air pressure to said molding material, and at least one exhaust hole located at a position adjoining said vent hole, but not facing said transfer surface.
 25. A mold assembly as claimed in claim 24 , said exhaust hole surrounds said vent hole.
 26. A mold assembly as claimed in claim 24 , wherein said exhaust hole is similar in configuration to a contour of said mold surface where said draft hole is present.
 27. A mold assembly as claimed in claim 24 , wherein said exhaust hole comprises a porous member.
 28. A mold assembly as claimed in claim 24 , wherein forced exhaustion means is communicated to said exhaust hole.
 29. A mold assembly as claimed in claim 24 , wherein said exhaust hole has an opening width of 0.001 mm to 0.5 mm.
 30. A method of producing a plastic molding, comprising the steps of: preparing a mold assembly including at least one transfer surface and at least one none-transfer surface formed on a surface other than said transfer surface, said transfer surface and said non-transfer surface forming at least one cavity; injecting molten resin heated to a temperature above a softening point thereof into said cavity; causing a resin pressure to act on said transfer surface to thereby cause said resin to adhere to said transfer surface, and then cooling said resin to a temperature below the softening point; opening said mold assembly in order to allow a resulting molding to be taken out; and lowering a temperature of at least one non-transfer surface of said resin below a temperature of said resin on said transfer surface during an interval between a beginning and an end of injection of said resin into said cavity.
 31. A method of producing a plastic molding, comprising the steps of: preparing a mold assembly including at least one transfer surface and at least one none-transfer surface formed on a surface other than said transfer surface, said transfer surface and said non-transfer surface forming at least one cavity; injecting molten resin heated to a temperature above a softening point thereof into said cavity; causing a resin pressure to act on said transfer surface to thereby cause said resin to adhere to said transfer surface, and then cooling said resin to a temperature below the softening point; opening said mold assembly in order to allow a resulting molding to be taken out; and forming a gas layer between at least one non-transfer surface of said resin and said mold assembly during an interval between a beginning and an end of injection of said resin into said cavity.
 32. A method of producing a plastic molding, comprising the steps of: preparing a mold assembly including at least one transfer surface and at least one none-transfer surface formed on a surface other than said transfer surface, said transfer surface and said non-transfer surface forming at least one cavity; injecting molten resin heated to a temperature above a softening point thereof into said cavity; causing a resin pressure to act on said transfer surface to thereby cause said resin to adhere to said transfer surface, and then cooling said resin to a temperature below the softening point; opening said mold assembly in order to allow a resulting molding to be taken out; and maintaining a portion of said mold assembly facing at least one non-transfer surface of said resin lower in temperature than a portion of said mold assembly facing said transfer surface until injection of said resin into said cavity ends.
 33. A method of producing a plastic molding, comprising the steps of: preparing a mold assembly including at least one transfer surface and at least one none-transfer surface formed on a surface other than said transfer surface, said transfer surface and said non-transfer surface forming at least one cavity; injecting molten resin heated to a temperature above a softening point thereof into said cavity; causing a resin pressure to act on said transfer surface to thereby cause said resin to adhere to said transfer surface, and then cooling said resin to a temperature below the softening point; opening said mold assembly in order to allow a resulting molding to be taken out; and effecting, during an interval between a beginning and an end of injection of said resin into said cavity, at least one of lowering a temperature of at least one non-transfer surface of said resin below a temperature of said resin on said transfer surface, forming a gas layer between at least one non-transfer surface of said resin and said mold assembly, and lowering a temperature of a portion of said mold assembly facing at least one non-transfer surface of said resin below a temperature of a portion of said mold assembly facing said transfer surface.
 34. A method of producing a plastic molding, comprising the steps of: preparing a mold assembly including at least one transfer surface and at least one none-transfer surface formed on a surface other than said transfer surface, said transfer surface and said non-transfer surface forming at least one cavity; injecting molten resin heated to a temperature above a softening point thereof into said cavity; causing a resin pressure to act on said transfer surface to thereby cause said resin to adhere to said transfer surface, and then cooling said resin to a temperature below the softening point; opening said mold assembly in order to allow a resulting molding to be taken out; effecting, during an interval between a beginning and and end of injection of said resin into said cavity, at least one of lowering a temperature of at least one non-transfer surface of said resin below a temperature of said resin on said transfer surface, forming a gas layer between at least one non-transfer surface of said resin and said mold, and lowering a temperature of a mold portion facing at least one non-transfer surface of said resin below a temperature of a mold portion facing said transfer surface; and pressing at least one non-transfer surface of said resin by a gas. 